Abstract
The structural factors such as crystal structure, particle size distribution and impurity content of hydrated TiO2 had great effects on the structures and pigment properties of the rutile TiO2. The rutile TiO2 white pigment was prepared via the Short Sulfate Process from low concentration industrial TiOSO4 solution. In order to produce rutile TiO2 pigment with good structures and excellent pigment properties, the crystal size of the hydrated TiO2 should be controlled less than 8.9 nm and as close as possible to 7.9 nm, which could effectively promote the phase transformation and crystal growth of the rutile TiO2. The appropriate particle size distribution of hydrated TiO2 had obvious effects on obtaining rutile TiO2 with narrower particle size distribution and near 0.20 µm. It was best to adjust the hydrolysis conditions to reduce the specific surface area of the hydrated TiO2 so as to reduce the iron ion impurity adsorption.