Abstract
BACKGROUND: The aim was to compare the dislodgement resistance of calcium silicate-based sealers (Total Fill BC Sealer, Endo CPM Sealer, BioRoot RCS) with an epoxy resin-based sealer (AH Plus). METHODS: The root canals of 80 single-rooted human teeth were instrumented with F360 up to size 45.04. All canals were obturated using matching gutta-percha cones according to the single-cone technique in combination with one of the mentioned sealers (n = 20 per group). After eight weeks of incubation (37 °C, 100% humidity), the roots were embedded in resin. Starting with a distance of 7 mm from the apex, four slices of 1 mm thickness were cut. Dislodgement resistance was measured using a universal testing machine and the push-out bond strength was calculated. Specimens were examined under 4×-magnification to determine the mode of bond failure. Statistical analysis was performed using ANOVA and Student-Newman-Keuls-test. RESULTS: Regarding the pooled data of all sections, the push-out bond strength of AH Plus was significantly higher than the push-out bond strength of all calcium silicate-containing sealers (P < 0.05). Out of all calcium silicate-based sealers, Total Fill BC Sealer showed the highest push-out bond strength (P < 0.05). BioRoot RCS had significant higher push-out bond strength than Endo CPM Sealer (P < 0.05). Nearly the same results were found for all four sections. BioRoot RCS only differed significantly from Endo CPM Sealer in the third section (P < 0.05). CONCLUSIONS: The push-out bond strength of the investigated calcium silicate-based sealers was lower than of AH Plus. Total Fill BC showed the highest push-out bond strength of the calcium silicate-based sealers.