Abstract
As a result of the emergence of two-dimensional (2D) materials for various opto-electronics applications, a new class of materials named MXenes have been attracting interests due to their outstanding nonlinear properties. In this work, an MXene niobium carbide (Nb(2)C) was proposed and demonstrated as a saturable absorber to induce mode-locking in thulium- and thulium/holmium-doped fiber lasers. The Nb(2)C solution was first prepared using the liquid exfoliation technique, and then deposited onto a microfiber for integration into the laser cavity. Stable mode-locking operation was observed in both laser cavities, where the center wavelengths of the laser were recorded at 1944 nm for the TDFL and 1950 nm for the THDFL. The generated pulses in the TDFL and THDFL had repetition rates of 9.35 and 11.76 MHz respectively, while their corresponding pulse widths were 1.67 and 1.34 ps. Both of the lasers were highly stable, having SNR values of more than 52 dB and showed no major fluctuations when tested for their long-term stabilities. The results demonstrate an excellent performance of the Nb(2)C as a saturable absorber, offering opportunities to further explore MXenes for future photonics devices.