Abstract
We report optical phonon vibration modes in ensembles of self-catalyzed InP/InAs/InP multi core-shell one-dimensional nanostructures (nanopillars and nanocones) grown on InP(111)B substrates using liquid indium droplets as a catalyst via metal-organic chemical vapor deposition. We characterized the Raman vibration modes of InAs E(1)(TO), InAs A(1)(TO), InAs E(1)(LO), InP E(1)(TO), InP A(1)(LO), and InP E(1)(LO) from the ensemble of as-grown nanostructures. We also identified second-order Raman vibration modes, associated with InP E(1)(2TO), E(1)(LO+TO), and E(1)(2LO), in the InP/InAs/InP core-shell nanopillars and nanocones. Raman spectra of InP/InAs/InP nanopillars showed redshift and broadening of LO modes at low-frequency branches of InAs and InP. Due to the polar nature in groups III-V nanowires, we observed strong frequency splitting between InAs E(1)(TO) and InAs A(1)(LO) in InP/InAs/InP nanocones. The Raman resonance intensities of InP and InAs LO modes are found to be changed linearly with an excitation power. By tilting the substrate relative to the incoming laser beam, we observed strong suppression of low-frequency branch of InP and InAs LO phonon vibrations from InP/InAs/InP nanocones. The integrated intensity ratio of InP E(1)(TO)/E(1)(LO) for both nanostructures is almost constant at 0-degree tilt, but the ratio of the nanocones is dramatically increased at 30-degree tilt. Our results suggest that Raman spectroscopy characterization with a simple substrate tilting method can provide new insights into non-destructive characterization of the shape, structure, and composition of the as-grown nanostructures for the wafer-scale growth and integration processing of groups III-V semiconducting hetero-nanostructures into nanoelectronics and photonics applications.