Abstract
It is highly expected to develop a simple and effective method to reinforce polyamide 6 (PA6) to enlarge its application potential. This is challenging because of frequently encountered multi-component phase separations. In this paper, we propose a novel method to solve this issue, essentially comprising two steps. Firstly, a kind of poly (amide-block-aramid) block copolymers, i.e., thermotropic liquid crystalline polymer (TLCP)-polyamide 6 (TLCP-PA6), that contains both rigid aromatic liquid crystal blocks, and flexible alkyl blocks were synthesized. It is unique in that TLCP is chemically linked with PA6, which is advantageous in excellent chemical and physical miscibility with the precursors of monomer casting polyamide 6 (MCPA6), i.e., ε-caprolactam. Secondly, such newly synthesized block copolymer TLCP-PA6 was dissolved in the melting ε-caprolactam, and followed by in situ polymerization to obtain composite polymer blends, i.e., MCPA6/TLCP-PA6. The thermodynamic, morphological, and crystalline properties of MCPA6/TLCP-PA6 can be easily manipulated by tailoring the loading ratios between TLCP-PA6 and ε-caprolactam. Especially, at the optimized condition, such MCPA6/TLCP-PA6 blends show an excellent miscibility. Systematic characterizations, including nuclear magnetic resonance (NMR), Fourier-transform infrared spectroscopy (FT-IR), differential scanning calorimeter (DSC), and polarizing optical microscope (POM), were performed to confirm these statements. In view of these results, it is anticipated that the overall mechanical properties of such PA6-based polymer composites will be satisfactory, which should enable applications in the modern plastic industry and other emerging areas, such as wearable fabrics.