Abstract
Facile synthesis of poly (N,N-dimethylaminoethyl methacrylate) (PDMAEMA) star polymers on the basis of the prepolymer chains, PDMAEMA as the macro chain transfer agent and divinyl benzene (DVB) as the cross-linking reagent by reversible addition-fragmentation chain transfer (RAFT) polymerization was described. The RAFT polymerizations of DMAEMA at 70 °C using four RAFT agents with different R and Z group were investigated. The RAFT agents used in these polymerizations were dibenzyl trithiocarbonate (DBTTC), s-1-dodecyl-s'-(α,α'-dimethyl-α-acetic acid) trithiocarbonate (MTTCD), s,s'-bis (2-hydroxyethyl-2'-dimethylacrylate) trithiocarbonate (BDATC) and s-(2-cyanoprop-2-yl)-s-dodecyltrithiocarbonate (CPTCD). The results indicated that the structure of the end-group of RAFT agents had significant effects on the ability to control polymerization. Compared with the above-mentioned RAFT agents, CPTCD provides better control over the molecular weight and molecular weight distribution. The polydispersity index (PDI) was determined to be within the scope of 1.26 to 1.36. The yields, molecular weight, and distribution of the star polymers can be tuned by changing the molar ratio of DVB/PDMAEMA-CPTCD. The chemical composition and structure of the linear and star polymers were characterized by GPC, FTIR, 1H NMR, XRD analysis. For the pure Chitosan membrane, a great improvement was observed for both CO₂ permeation rate and ideal selectivity of the blending composite membrane upon increasing the content of SPDMAEMA-8. At a feed gas pressure of 37.5 cmHg and 30 °C, the blinding composite membrane (Cs: SPDMAEMA-8 = 4:4) has a CO₂ permeation rate of 8.54 × 10⁻⁴ cm³ (STP) cm⁻²∙s⁻¹∙cm∙Hg⁻¹ and a N₂ permeation rate of 6.76 × 10⁻⁵ cm³ (STP) cm⁻²∙s⁻¹∙cm∙Hg⁻¹, and an ideal CO₂/N₂ selectivity of 35.2.