Abstract
An expired metformin drug (MET) was used as a corrosion inhibitor for C1018 carbon steel in a CO(2)-saturated 3.5 wt % NaCl + 340 ppm acetic acid solution under static conditions. The inhibitor was evaluated using electrochemical methods complemented with surface analytical measurements and computational modeling. The drug displayed a high inhibition efficiency of ∼90% at 200 ppm. Impedance analyses revealed a rise in the charge transfer resistance at the steel-solution interface upon the addition of the inhibitor. Polarization measurements suggested that MET acted more like a cathodic-type corrosion inhibitor and significantly reduced the corrosion current density. The adsorption of MET on the steel substrate followed the Langmuir isotherm, showing a mixed type of physical and chemical modes of adsorption. The thermodynamic parameters revealed strong and spontaneous adsorption on the steel surface. The surface analysis using SEM supported the inhibitor adsorption on the steel substrate. Based on the DFT simulation, inhibition by MET is mainly achieved by its protonated form, which leads to the formation of a thin film on the steel surface rather than the modification of the work function of the steel surface. The experimental and theoretical estimations of pKa complemented the DFT results, both agreeing that the monoprotonated form of MET is the dominant form in which the inhibitor adsorbs on the steel surface to form a thin film rather than modify the work function of the steel surface.