Abstract
TiO(2) films with a three-dimensional web-like porous structure were prepared using the photo polymerization-induced phase separation method integrated with the pulling coating process. By adjusting the ratio of the substance in the precursor sol and the coating times, the relationships between the sol ratio, the coating times, the film structure, and the performance of the DSC were studied. The optimal film structure was found and a detailed description is given. The performance of the DSC was further improved by introducing the barrier layer and the surface-modified layer of the TiO(2) coating. This promoted the short-circuit current density and the photoelectric conversion efficiency of the DSC, the mechanism of which was also investigated. Ultimately, the photoelectric conversion efficiency of the DSC based on the TiO(2) anode films with a three-dimensional web-like structure was stabilized at a higher level as a result of the structural improvement.