Abstract
To better understand the complex interplay of speed and environment on metals commonly used in implants, rotary bend fatigue tests were conducted on stainless steel and nitinol wires. A range of alternating strains was tested to create ε-N curves at two speeds (physiologic and accelerated) and in three environments (deionized water at body temperature, phosphate buffered saline at body temperature, and laboratory air at ambient room temperature). Results indicate that speed and environment can affect the observed fatigue life in nuanced ways. An electropotential monitoring technique was demonstrated to characterize fatigue crack growth which may be useful in future investigations.