Abstract
To investigate the influence of Zn-alloying on the microstructure and tensile mechanical properties of Mg-6Bi alloy after hot extrusion, a new ternary Mg-6Bi-3Zn alloy was prepared by extrusion at 300 °C. The microstructures, texture, dynamic precipitates and tensile mechanical behaviors of the extruded alloy were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), electron backscattered diffraction (EBSD) and a material testing machine at room temperature. After extrusion, the Mg-6Bi-3Zn alloy possesses a bimodal microstructure with elongated large unrecrystallized (unDRXed) grains and fine dynamic recrystallized (DRXed) grains. In addition, non-basal <202_1>//ED, <448_3>//ED and <112_1>//ED textures are observed within DRXed grains due to the Zn addition, leading to texture weakening in the extruded Mg-6Bi-3Zn alloy. Zn addition facilitates the dynamic precipitation behavior, leading to a 12.2% area fraction of Mg(3)Bi(2) precipitates with an average size of 39.2 nm. Furthermore, incorporation of Zn atoms in Mg(3)Bi(2) phases and segregation of Zn at the grain boundary are found. The extruded Mg-6Bi-3Zn alloy exhibits a tensile strength of 336 ± 7.1 MPa and a yield strength of 290 ± 5.5 MPa, as well as an elongation of 11.5%. Therefore, Zn addition is beneficial to enhance strength and keep good ductility for the extruded Mg-6Bi-3Zn alloy.