Abstract
In this paper, novel colorless polyimides (PIs) derived from 5,5'-bis(2,3-norbornanedicarboxylic anhydride) (BNBDA) were presented. The results of single-crystal X-ray structural analysis using a BNBDA-based model compound suggested that it had a unique steric structure with high structural linearity. Therefore, BNBDA is expected to afford new colorless PI films with an extremely high glass transition temperature (Tg) and a low linear coefficient of thermal expansion (CTE) when combined with aromatic diamines with rigid and linear structures (typically, 2,2'-bis(trifluoromethyl)benzidine (TFMB)). However, the polyaddition of BNBDA and TFMB did not form a PI precursor with a sufficiently high molecular weight; consequently, the formation of a flexible, free-standing PI film via the two-step process was inhibited because of its brittleness. One-pot polycondensation was also unsuccessful in this system because of precipitation during the reaction, probably owing to the poor solubility of the initially yielded BNBDA/TFMB imide oligomers. The combinations of (1) the structural modification of the BNBDA/TFMB system, (2) the application of a modified one-pot process, in which the conditions of the temperature-rising profile, solvents, azeotropic agent, catalysts, and reactor were refined, and (3) the optimization of the film preparation conditions overcame the trade-off between low CTE and high film toughness and afforded unprecedented PI films with well-balanced properties, simultaneously achieving excellent optical transparency, extremely high Tg, sufficiently high thermal stability, low CTE, high toughness, relatively low water uptake, and excellent solution processability.