Circular economy reinforcement through molecular fabrication of textile wastes with microbial synthesized ZnO nanoparticles to have multifunctional properties.

The fibrous wastes generated from the mills of textile production can be recycled and converted into high add-values products to be implemented in several applications. The current study aimed to employ commercial free cellulase enzyme to partially hydrolyze (activate) the polyester cotton blended (PET/C) fibrous wastes by creation functional groups such as OH and COOH on their surfaces. The activated fibrous wastes were then modified by coating with ZnO nanoparticles (ZnO-NPs) biosynthesized by actinobacterial cultures free supernatant. The isolate was identified as Streptomyces pseudogriseolus with accession number of OR574241. The conditions that influence the actino-synthesis of ZnO-NPs were optimized and the product was characterized using spectroscopic vision, FTIR, XRD, TEM and SEM. The characteristic ZnO peaks were obviously observed by EDX analysis with 0.38 and 0.75% (wt%), respectively. TEM analyses proved the nanoscale of ZnO-NPs (5-15 nm) which was followed by cytotoxic evaluation for the produced NPs. Fortunately, the tested actino-ZnO-NPs didn't have any cytotoxicity against human normal fibroblast cell line (BJ1), which means that the product can be safely used in a direct-contact with human skin. The treated PET/C blended waste fabrics coated with ZnO-NPs showed high antimicrobial activity and ultraviolet protection values after functionalization by cellulase. EDX analysis demonstrates the presence of Zn peaks on the coated fabrics compared with their absence in blank and control samples, while SEM images showed the formation of a thin layer of ZnO-NPs on the fabric surface. The obtained smart textile can be applied several needed sectors.