Comparative Evaluation of Mechanical Properties and Color Stability of Dental Resin Composites for Chairside Provisional Restorations.

Resin composites have become the preferred choice for chairside provisional dental restorations. However, these materials may undergo discoloration, changes in surface roughness, and mechanical properties with aging in the oral cavity, compromising the aesthetics, functionality, and success of dental restorations. To investigate the color and mechanical stability of chairside provisional composite resins, this study evaluated the optical, surface, and mechanical properties of four temporary restoration resin materials before and after aging, stimulated by thermal cycling in double-distilled water. Measurements, including CIE LAB color analysis, three-point bending test, nanoindentation, scanning electron microscopy (SEM), and atomic force microscopy (AFM), were conducted (n = 15). Results showed significant differences among the materials in terms of optical, surface, and mechanical properties. Revotek LC (urethane dimethacrylate) demonstrated excellent color stability (ΔE(00) = 0.53-Black/0.32-White), while Artificial Teeth Resin (polymethyl methacrylate) exhibited increased mechanical strength with aging (p < 0.05, FS = 68.40 MPa-non aging/87.21 MPa-aging). Structur 2 SC (Bis-acrylic) and Luxatemp automix plus (methyl methacrylate bis-acrylate) demonstrated moderate stability in optical and mechanical properties (Structur 2 SC: ΔE(00) = 1.97-Black/1.38-White FS = 63.20 MPa-non aging/50.07 MPa-aging) (Luxatemp automix plus: ΔE(00) = 2.49-Black/1.77-White FS = 87.72 MPa-non aging/83.93 MPa-aging). These results provide important practical guidance for clinical practitioners, as well as significant theoretical and experimental bases for the selection of restorative composite resins.