Synergistic effect of trivalent (Gd(3+), Sm(3+)) and high-valent (Ti(4+)) co-doping on antiferromagnetic YFeO(3).

Monophasic polycrystalline powders of Y(1-x) R (x) Fe(1-(4/3)y) Ti (y) O(3) (R = Sm, Gd; x = 0.05, 0.10, 0.15; y = 0.05) were successfully synthesized via a low temperature solid-state synthesis route. The X-ray diffraction and Raman spectroscopy studies indicate that all the calcined powders with R(3+) (Gd(3+), Sm(3+)) at Y(3+) and Ti(4+) at Fe(3+) sites were crystallized in an orthorhombic phase associated with a change in lattice parameters. The Williamson-Hall method employed to calculate the strain revealed that the strain increased with the increased concentration of dopants ((Gd(3+), Sm(3+)) at Y(3+)) compared to an increase in the size of crystallites, corroborating the findings of SEM. Analysis of diffuse reflectance spectra indicated a drop in bandgap from 1.93 eV to 1.86 eV and 1.96 eV to 1.91 eV for Gd, Ti co-doping and Sm, Ti co-doping respectively, demonstrating the capacity of the synthesized powders to absorb visible light. Absorbance spectra also revealed the existence of mixed states of Fe(3+) and Fe(4+) which was corroborated by XPS studies. The magnetic hysteresis loop analysis at room temperature illustrated that with co-doping, there is a strong enhancement in magnetization as well as coercivity, suggesting a strong transition from anti-ferromagnetic behaviour to ferromagnetic behaviour. Pertaining to the greatly improved optical and magnetic properties with the addition of (Gd(3+), Sm(3+)) at Y(3+) and Ti(4+) at Fe(3+) sites, these materials are anticipated to be of potential use in various applications.