Adsorption of Chromium and Nickel Ions on Commercial Activated Carbon-An Analysis of Adsorption Kinetics and Statics.

The adsorption of nickel Ni(II) and chromium Cr(III) ions on the commercial activated carbons WG-12, F-300 and ROW 08, which differ in their pore structure and the chemical nature of their surfaces, were analyzed. The nickel ions Ni(2+) were best adsorbed on the WG-12 activated carbon, which had the largest number of carboxyl and lactone groups on the surface of the activated carbons, and the largest specific surface area. Chromium, occurring in solutions with pH = 6 in the form of Cr(OH)(2+) and Cr(OH)(2)(+) cations, was best adsorbed on the ROW 08 Supra activated carbon, which is characterized by the highest values of water extract. The precipitation of chromium hydroxide in the pores of the activated carbon was the mechanism responsible for the high adsorption of Cr(III) on this carbon. For the other sorbents, the amount of carboxyl and lactone groups determined the amount of Cr(III) and Ni(II) adsorption. The adsorption kinetics results were described with PFO, PSO, Elovich and intraparticle diffusion models. The highest correlation coefficients for both the Cr(III) and Ni(II) ions were obtained using the PSO model. Among the seven adsorption isotherm models, very high R(2) values were obtained for the Toth, Temkin, Langmuir and Jovanovic models. The Cr(III) ions were removed in slightly larger quantities than the Ni(II) ions. The capacities of the monolayer q(m) (calculated from the Langmuir isotherm) ranged from 55.85 to 63.48 mg/g for the Cr(III), and from 40.29 to 51.70 mg/g for the Ni(II) ions (pH = 6). The adsorption efficiency of Cr(III) and Ni(II) cations from natural waters with different degrees of mineralization (spring, weakly and moderately mineralized) was only a few percent lower than that from deionized water.