Bi(1-x)Eu(x)FeO(3) Powders: Synthesis, Characterization, Magnetic and Photoluminescence Properties.

Europium substituted bismuth ferrite powders were synthesized by the sol-gel technique. The precursor xerogel was characterized by thermal analysis. Bi(1-x)Eu(x)FeO(3) (x = 0-0.20) powders obtained after thermal treatment of the xerogel at 600 °C for 30 min were investigated by X-ray diffraction (XRD), scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), Raman spectroscopy, and Mössbauer spectroscopy. Magnetic behavior at room temperature was tested using vibrating sample magnetometry. The comparative results showed that europium has a beneficial effect on the stabilization of the perovskite structure and induced a weak ferromagnetism. The particle size decreases after the introduction of Eu(3+) from 167 nm for x = 0 to 51 nm for x = 0.20. Photoluminescence spectroscopy showed the enhancement of the characteristic emission peaks intensity with the increase of Eu(3+) concentration.