Application of Statistical Methods to Accurately Assess the Effect of Gamma Aluminum Oxide Nanopowder on the Hardness of Composite Materials with Polyester-Glass Recyclate.

Polymer composites are materials that are used in many industries. Their wide application has a direct impact on the amount of post-production and post-consumer waste. The global problem with recycling, especially of fiber-reinforced polymeric materials, has prompted research into methods of their use. Previous research on composite materials with polyester-glass recyclate showed a decrease in mechanical properties. The construction material should have the highest mechanical properties. Based on the literature, it was found that the use of nanoadditives may have a positive effect on the parameters of the materials. The use of gamma aluminum nanopowder, in a small amount can significantly increase the mechanical properties of composites with polyester-glass recyclate, and thus can affect the application of these materials to structural elements. The article is devoted to the research on the hardness of composite materials with polyester-glass recyclate and gamma aluminum nanopowder. The main goal is to investigate the possibility of using a nanoadditive as a material, increasing the mechanical properties of composites with polyester-glass recyclate, so as to create a recycled material with the highest possible strength parameters. Hardness tests were performed using the Barcol method. For each composite material, 30 measurements were made in order to subject the results to a statistical analysis. Using parametric statistical tests it was shown that the obtained hardness values at the assumed level of statistical significance p(v) = 0.05 for comparisons for the samples of the reference material (B0) do not differ by chance, while for the comparisons in the configurations of the reference material (B0) with the modified materials, (R10, A2, R10A2) they do not differ by accident. Studies have shown that the addition of 2% gamma aluminum nanopowder slightly lowers the hardness of a pure polyester-glass composite, but the same additive allows the hardness of composite materials to be increased with the addition of glass recyclate. This is of particular importance for the development of the optimal composition of polyester-glass composites with the addition of recyclate, which will have good strength properties and at the same time enable the reuse of composite waste.