Notches and Fatigue on Aircraft-Grade Aluminium Alloys.

The influence of notches and fatigue on the ultimate tensile strength and elongation at break of aluminium alloys (2024-T3, 6061-T4, 6061-T4 uncoated, 6061-T6 uncoated, 7075-T0, and 7076-T6) is presented in this study. A total of 120 specimens were used. On all specimens, notches were made using a CNC machine, with 60 of them subjected to low-cycle fatigue (LCF) before undergoing the tensile test. Based on the statistical examination of the measured data, mathematical prediction models have been established. Compared to their unscratched counterparts, the results indicate a significant decrease in the UTS and elongation at break for both notched and notched-fatigued specimens. The LCF pre-treatment contributes to the negative impacts of the notches, resulting in reduced values for the UTS and elongation at break, thus concluding that surface integrity is critical for maintaining the structural strength of aircraft components.