Porous Cu-MOF nanostructures with anticancer properties prepared by a controllable ultrasound-assisted reverse micelle synthesis of Cu-MOF.

The ultrasonic assisted reverse micelle method (UARM) was used to synthesize Cu-MOF from Cu(NO(3))(2)·3H(2)O and 2,6-pyridine dicarboxylic acid in a 1:1 molar proportion. It has been characterized using FT-IR, XRD, nitrogen adsorption analysis, SEM and TEM-EDX. The morphology of Cu-MOFs was spherical, with an average particle size distribution of less than 100 nm. Using BET analysis, the surface area of Cu-MOF was found to be 284.94 m(2)/g. The porous morphology of Cu-MOF was also suggested by SEM and TEM analyses. It has anticancer properties against MCF-7 breast cancer cells. Cytotoxicity testing was performed on MCF-7 breast cancer cells using the MTT cell viability assay, and cell proliferation and viability were found to be approximately 24% higher than the control.