Refinement of Sustainable Polybutylene Adipate Terephthalate (PBAT) with Amorphous Hydrogenated Carbon Films (a-C:H) Revealing Film Instabilities Influenced by a Thickness-Dependent Change of sp(2)/sp(3) Ratio.

The increasing use of polymers is related to a growing disposal problem. Switching to biodegradable polymers such as polybutylene adipate terephthalate (PBAT) is a feasible possibility, but after industrial production of commercially available material PBAT is not suitable for every application. Therefore, surface refinements with amorphous hydrogenated carbon films (a-C:H) produced by plasma-assisted chemical vapor deposition (PE-CVD) changing the top layer characteristics are used. Here, 50 µm-thick PBAT films are coated with a-C:H layers up to 500 nm in 50 nm steps. The top surface sp(2)/sp(3) bonding ratios are analyzed by X-ray photoelectron spectroscopy (XPS) and near-edge X-ray absorption fine structure (NEXAFS) both synchrotron-based. In addition, measurements using diffuse reflectance infrared Fourier transform spectroscopy (DRIFT) were performed for detailed chemical composition. Surface topography was analyzed by scanning electron microscopy (SEM) and the surface wettability by contact angle measurements. With increasing a-C:H layer thickness not only does the topography change but also the sp(2) to sp(3) ratio, which in combination indicates internal stress-induced phenomena. The results obtained provide a more detailed understanding of the mostly inorganic a-C:H coatings on the biodegradable organic polymer PBAT via in situ growth and stepwise height-dependent analysis.