Nitrogen-Doped Diamond-like Coatings for Long-Term Enhanced Cell Adhesion on Electrospun Poly(ε-caprolactone) Scaffold Surfaces.

Electrospun poly(ε-caprolactone) (PCL)-based scaffolds are widely used in tissue engineering. However, low cell adhesion remains the key drawback of PCL scaffolds. It is well known that nitrogen-doped diamond-like carbon (N-DLC) coatings deposited on the surface of various implants are able to enhance their biocompatibility and functional properties. Herein, we report the utilization of the pulsed vacuum arc deposition (PVAD) technique for the fabrication of thin N-DLC coatings on the surface of electrospun PCL scaffolds. The effect of N-DLC coating deposition under various nitrogen pressures on the morphological, mechanical, physico-chemical, and biological properties of PCL scaffolds was investigated. It was established that an increase in nitrogen pressure in the range from 5 × 10(-3) to 5 × 10(-1) Pa results in up to a 10-fold increase in the nitrogen content and a 2-fold increase in the roughness of the PCL fiber surface. These factors provided the conditions for the enhanced adhesion and proliferation of human mesenchymal stem cells (MMSCs) on the surface of the modified PCL scaffolds. Importantly, the preservation of N-DLC coating properties determines the shelf life of a coated medical device. The elemental composition, tensile strength, and surface human MMSC adhesion were studied immediately after fabrication and after 6 months of storage under normal conditions. The enhanced MMSC adhesion was preserved after 6 months of storage of the modified PCL-based scaffolds under normal conditions.