Impact of Polymer Physicochemical Features on the Amorphization and Crystallization of Citric Acid in Solid Dispersions.

The amorphization and crystallization of citric acid in the presence of a variety of polymers were investigated. Polymers were chosen for their different physicochemical features, including hygroscopicity, glass transition temperature (T(g)), and functional groups capable of forming intermolecular non-covalent interactions with citric acid. Citric acid solutions with varying amounts of pectin (PEC), guar gum (GG), κ-carrageenan (KG), gelatin (GEL), (hydroxypropyl)methylcellulose (HPMC), and carboxymethylcellulose sodium (CMC-Na) were lyophilized. Dispersions were stored for up to 6 months in controlled temperature and relative humidity environments and periodically monitored using powder X-ray diffraction, differential scanning calorimetry, and Fourier transform infrared spectroscopy. Moisture sorption isotherms and moisture contents were determined. Amorphous solid dispersions of citric acid were successfully formed in the presence of ≥20% w/w CMC-Na and PEC or ≥30% w/w of the other polymers except KG which required a minimum of 40% polymer. All samples remained amorphous even in their rubbery state at 0% RH (25 °C and 40 °C), but increasing the RH to 32% RH resulted in citric acid crystallization in the KG dispersions, and further increasing to 54% RH resulted in crystallization in all samples. Polymer effectiveness for inhibiting citric acid crystallization was CMC-Na > PEC ≥ GEL > HPMC > GG > KG. To create and maintain amorphous citric acid, polymer traits in order of effectiveness were as follows: greater propensity for intermolecular non-covalent interactions (both ionic and hydrogen bonding) with the citric acid, carbonyl groups, higher T(g), and then lower hygroscopicity.