Elaboration and Characterization of Electrodes from Robinia pseudoacacia and Azadirachta indica Charcoal Powder with Coconut Bio-Pitch as a Binder.

Carbon-based electrodes have recently been most widely used in P-MFC due to their desirable properties such as biocompatibility, chemical stability, affordable price, corrosion resistance, and ease of regeneration. In general, carbon-based electrodes, particularly graphite, are produced using a complex process based on petroleum derivatives at very high temperatures. This study aims to produce electrodes from bio-pitch and charcoal powder as an alternative to graphite electrodes. The carbons used to manufacture the electrodes were obtained by the carbonisation of Robinia pseudoacacia and Azadirachta indica wood. These carbons were pulverised, sieved to 50 µm, and used as the raw materials for electrode manufacturing. The binder used was bio-pitch derived from coconut shells as the raw materials. The density and coking value of the bio-pitch revealed its potential as a good alternative to coal-tar pitch for electrode manufacturing. The electrodes were made by mixing 66.50% of each carbon powder and 33.50% of bio-pitch. The resulting mixture was moulded into a cylindrical tube 8 mm in diameter and 80 mm in length. The raw electrodes obtained were subjected to heat treatment at 800 °C or 1000 °C in an inert medium. The electrical resistivity obtained by the four-point method showed that N1000 has an electrical resistivity at least five times lower than all the electrodes developed and two times higher than that of G. Fourier-transform infrared spectroscopy (FTIR) was used to determine the compositional features of the samples and their surface roughness was characterised by atomic force microscopy (AFM). Charge transfer was determined by electrical impedance spectroscopy (EIS). The FTIR of the electrodes showed that N1000 has a spectrum that is more similar to that of G compared to the others. The EIS showed the high ionic mobility of the ions and therefore that N1000 has a higher charge transfer compared to G and the others. AFM analysis revealed that N1000 had the highest surface roughness in this study.