The influence Cl(-) on stress corrosion of 7xxx series aluminium alloys studied by experimental and simulation technology.

The stress corrosion behavior of 7xxx series aluminium alloys in different concentrations NaCl solution was studied, and numerical simulation was conducted in COMSOL Multiphysics based on experimental results. Different stresses were applied on the experiment pieces, the pitting crater deepened with the change of stress level. The corrosion rate increased with the raising stress. There is no positive correlation between stress corrosion degree and chloride ion concentration. The most severe corrosion occurs in 5.0 wt% NaCl solution instead of 6.0 wt% NaCl solution due to the increase of water film conductivity and decrease of solubility of oxygen under high Cl(-) environment. The finite element model was used to analyze the stress distribution on aluminium alloy surface, to describe the dynamic equation of anodic dissolution of metal due to elastic and plastic deformation. Corrosion occurs mainly in stress concentrated areas. When the stress loading exceeds a certain threshold, plastic strain occurs on the surface of both the specimen and the structural part, the corrosion current density increases instantaneously, and the corrosion behavior in the stress concentration area gradually intensifies. The survey can provide practical theoretical guidance for predicting stress corrosion and extending the service life of equipment in (harsh) marine environments.