Composition, processing, and properties of biphasic zirconia bioceramics: relationship to competing strength and optical properties.

A study is made of relationships between composition, processing, structure and properties of biphasic zirconia bioceramics. The focus is on zirconia compositions with different yttria dopant contents used in modern dental restorations, namely 3 - 5 mol% yttria stabilized zirconia (3YSZ, 4YSZ, and 5YSZ). Crystallographies and densities are surveyed, sintering conditions examined, and microstructures characterized. Strength and optical tests are conducted on each YSZ, and dependencies on sintering temperature, cubic content and grain size analyzed. Strength correlates with the amount of tetragonal zirconia (t-ZrO(2)) crystals with large lattice distortions (tetragonality). YSZ translucency correlates with content of cubic zirconia (c-ZrO(2)) and t-ZrO(2) with low levels of tetragonality. Consistent with literature reporting, the materials rank in decreasing order 3YSZ, 4YSZ to 5YSZ for strength but increasing order for translucency. However, for a given composition, the data suggest that the strengths of densely sintered 3YSZ and 4YSZ actually increase with translucency, although that of 5YSZ remains undiminished. These trends are in apparent contradiction to prevailing experience, and offer potential future processing routes to optimization of clinical materials.