Abstract
Temperature response double network (DN) hydrogels comprising a network formed by polymerization of methacrylic acid (MA) modified PVA, N,N'-methylene bis(acrylamide), N-isopropylacryl amide (NIPAM), and one formed from crystalline polyvinyl alcohol (PVA) are prepared in a 3D printed tailor-made mold. The (PVA-MA)-g-PNIPAAm thermoset intermediate is formed in water by a radical, photo-initiated process, and in the presence of dissolved PVA polymers. A subsequent freezing-thawing sequence induces the crystallization of the PVA network, which forms a second network inside the thermoset NIPAM polymer. The prepared hydrogel is thermoresponsive by the phase transition of PNIPAAm segments (T ≈ 32 °C) and has good mechanical properties (tensile strength 1.23 MPa, compressive strength 1.47 MPa). Thermal cycling between room temperature at 40 or 50 °C shows the product converses from a virgin-state to a steady-state, which most likely involves the reorganization of PVA crystals. The swelling-deswelling cycles remain clear at a length change of about 13%.