Background
The
Conclusions
The recycled PET from waste bottles was successfully used to prepare porous membrane. The membrane was modified by the addition of PVP as a membrane modifying agent. SEM analysis confirmed that the original PET membrane has a rough and large pore structure. The addition of PVP improved the pore density with a narrow pore structure. The PET/PVP membrane conditioned with evaporation was the best in humic acid rejection.
Methods
Porous polymeric membranes were prepared via thermally induced phase separation by dissolving recycled PET in phenol. PET polymer was obtained from waste plastic bottles as a new source of polymeric material. For original PET membrane, the casting solution was prepared by dissolving of 20wt% PET in phenol solution. For PET modified membrane, a 5 wt% of polyvinylpyrrolidone (PVP) was added into polymer solution. The solution was cast onto a glass plate at room temperature followed by evaporation before the solidification process. The membranes formed were characterized in terms of morphology, chemical group, and filtration performance. A humic acid solution was used to identify the permeability and the solute rejection of the membranes.
Results
The results showed that the recycled PET from waste plastic bottles was applicable to use as a membrane material for a water treatment process. The maximum flux of 97.0 l/m 2.hr was obtained from filtration test using PET membrane. The highest rejection of humic acid in a water sample, which reached up to 75.92%, was obtained using the PET/PVP membrane. Conclusions: The recycled PET from waste bottles was successfully used to prepare porous membrane. The membrane was modified by the addition of PVP as a membrane modifying agent. SEM analysis confirmed that the original PET membrane has a rough and large pore structure. The addition of PVP improved the pore density with a narrow pore structure. The PET/PVP membrane conditioned with evaporation was the best in humic acid rejection.