Abstract
BACKGROUND: The aim of this investigation was to assess the effects of different treatments of demineralised enamel on microleakage under orthodontic brackets. METHODS: Seventy-five intact premolars were randomly assigned to five groups. The teeth in groups 2 through 5 were immersed in a demineralising solution for 16 weeks. In groups 1 (control) and 2 (demineralised/control), conventional acid etching was used. In group 3, sodium hypochlorite (NaOCl) was applied on the enamel surface for 1 min after acid etching, and in group 4, Transbond Plus (3M Unitek, Monrovia, CA, USA) self-etching primer (SEP) was used. The teeth in group 5 were treated with 2% sodium fluoride (NaF) for 4 min before etching. After bracket bonding, the specimens were thermocycled, sealed with nail varnish, immersed in 0.5% basic fuchsine solution for 24 h and sectioned. Microleakage was measured under a stereomicroscope for the enamel-adhesive and adhesive-bracket interfaces of both occlusal and gingival sides. RESULTS: Demineralised teeth showed more microleakage at the enamel-adhesive interface on both occlusal and gingival sides compared to sound teeth, but the difference was not significant (P>0.005). Treating the demineralised enamel with 5% NaOCl or Transbond Plus SEP was not effective in reducing microleakage. NaF treatment followed by acid etching of demineralised enamel resulted in significantly lower microleakage in most comparisons (P<0.005). CONCLUSIONS: The use of 2% NaF on hypomineralised enamel before the bracket bonding procedure is an effective way to decrease microleakage.