Abstract
The characteristics of magnetostructural coupling play a crucial role in the magnetic field-driven behaviour of magnetofunctional alloys. The availability of magnetostructural coupling over a broad temperature range is of great significance for scientific and technological purposes. This work demonstrates that strong magnetostrucural coupling can be achieved over a wide temperature range (222 to 355 K) in Co-doped high Mn-content Mn(50)Ni(42-x) Co (x) Sn(8) (0 ≤ x ≤ 10) melt-spun ribbons. It is shown that, over a wide composition range with Co content from 3 to 9 at.%, the paramagnetic austenite first transforms into ferromagnetic austenite at T(C) on cooling, then the ferromagnetic austenite further transforms into a weakly magnetic martensite at T(M). Such strong magnetostructural coupling enables the ribbons to exhibit field-induced inverse martensitic transformation behaviour and a large magnetocaloric effect. Under a field change of 5 T, a maximum magnetic entropy change ΔS(M) of 18.6 J kg(-1) K(-1) and an effective refrigerant capacity RC(eff) of up to 178 J kg(-1) can be achieved, which are comparable with or even superior to those of Ni-rich Ni-Mn-based polycrystalline bulk alloys. The combination of high performance and low cost makes Mn-Ni-Co-Sn ribbons of great interest as potential candidates for magnetic refrigeration.