Abstract
This study assessed the bond strength of prefabricated post systems at different root levels of endodontically treated teeth. One-rooted human premolars (N = 70; n = 10) were cut to 2 mm above the cement-enamel junction. Root canals were treated and randomly assigned to one of the seven post systems: T: Titanium (Mooser), ZrO: Zirconia (Cosmopost), G: Fiber (FRC Postec Plus), E1: Fiber (Direct) (Everstick post), E2: Fiber (Indirect) (Everstick post), PP: Fiber (PinPost), and LP: Injectable Resin/Fiber composite (EverX Posterior). All posts were luted using a resin cement (Variolink II), and the roots were sectioned at the coronal, middle, and apical root levels. Push-out tests were performed in the Universal Testing Machine (0.5 mm/min). Data (MPa) were analyzed using two-way ANOVA and Tukey's tests (α = 0.05). The results showed that the bond strength (mean ± SD) of E2 posts were highest (5.3 ± 2.7) followed by PP (4.1 ± 2.0); G (4.0 ± 1.6); LP (2.6 ± 1.9): T (2.2 ± 1.5) and ZrO (1.9 ± 1.0) posts systems. No significant differences were found in bond strength of all post systems. The bond strength in the coronal root level was the highest with 3.6 ± 2.2 MPa. The bond strength of FRC post systems was significantly higher than those of rigid posts of titanium or ZrO(2). Bond strength results were the highest in the coronal root level for all tested post systems but did not differ significantly from the other two root levels.