Abstract
Wood dyeing is an effective way to alleviate the supply-demand imbalance of valuable wood and improve the surface decoration of fast-growing wood. However, applications of dyed wood are limited due to the susceptibility of dyes and wood to photo-discolor and degrade under light irradiation. Thus, the improved weather resistance of dyed wood is crucial. To prevent photochromic discoloration of dyed wood, an anti-photochromic coating structure was constructed via layer-by-layer self-assembly (LbL) using chitosan and zinc oxide (ZnO). The results showed that the surface color difference of treated dyed wood was reduced by approximately 84.6% after the first 2 h of irradiation under the following conditions °C: temperature (50 °C), relative humidity (55%), and irradiation intensity (550 W/m(2)). However, the color of untreated dyed wood drastically changed at this stage. The reason for the decrease was that the redness and yellowness of treated dye wood were significantly reduced. The deposition of ZnO onto treated dyed wood helped to protect the wood from UV light irradiation. Chitosan bridged the dyes and complexed ZnO to enhance UV resistance. This study provides valuable information for the protection of dyed wood against light discoloration that can be used as an interior and exterior decorative material.