Conclusion
It may be concluded that using a bonding agent as a surface sealant does not increase stain resistance of resin composites of the sealants evaluated. Biscover LV showed the highest efficacy to prolong color stability of the resin composite.
Methods
28 disc-shaped materials were prepared from a nano-hybrid resin composite Filtek Z550 and assigned to four groups: G1K: nonsealed; G2:Adper Single Bond; G3: Fortify ; G4: Biscover LV. After 24 h storage in distilled water at 37˚C, all specimens were subjected to thermocycling and immersed into coffee solution. Color measurements were performed using spectrophotometer (VITA Easyshade; Vident) according to CIEL*a*b* system.
Purpose
This study investigated the influence of sealant application on stain resistance of a nanohybrid resin composite compared to the efficacy of a bonding agent used as a surface sealant on prolonging color stability of the resin composite. Materials and
Results
Color change values were significantly different among the groups in each evaluation period except for after thermocycling (p<0.05). For 7 days evaluation period, the difference between G3 and G4 group was statistically significant while G4 exhibited statistically significant differences (p<0.05 and p<0.0001 respectively) compared to control (G1) in 14 day whereas no significant difference was found between GI and GII in 28-day evaluation period. However, ΔE values of sealed specimens (GIII, GIV) differed significantly from non-sealed (GI) specimens after 28 days of immersion in coffee solution (p<0.05 and p<0.0001 respectively).