Abstract
Polybrominated diphenyl ethers (PBDEs) are recognized as a new class of widely-distributed and persistent contaminants for which effective treatment and remediation technologies are needed. In this study, two kinds of commercially available nanoscale Fe(0) slurries (Nanofer N25 and N25S), a freeze-dried laboratory-synthesized Fe(0) nanoparticle (nZVI), and their palladized forms were used to investigate the effect of particle properties and catalyst on PBDE debromination kinetics and pathways. Nanofers and their palladized forms were found to debrominate PBDEs effectively. The laboratory-synthesized Fe(0) nanoparticles also debrominated PBDEs, but were slower due to deactivation by the freeze-drying and stabilization processes in the laboratory synthesis. An organic modifier, polyacrylic acid (PAA), bound on N25S slowed PBDE debromination by a factor of three to four compared to N25. The activity of palladized nZVI (nZVI/Pd) was optimized at 0.3 Pd/Fe wt% in our system. N25 could debrominate selected environmentally-abundant PBDEs, including BDE 209, 183, 153, 99, and 47, to end products di-BDEs, mono-BDEs and diphenyl ether (DE) in one week, while nZVI/Pd (0.3 Pd/Fe wt%) mainly resulted in DE as a final product. Step-wise major PBDE debromination pathways by unamended and palladized Fe(0) are described and compared. Surface precursor complex formation is an important limiting factor for palladized Fe(0) reduction as demonstrated by PBDE pathways where steric hindrance and rapid sequential debromination of adjacent bromines play an important role.