Conclusions
MEP pretreatment presented the lowest SBS values, regardless the silicate ceramic and aging level. Further research is necessary. Clinical relevance: There is no need for intraoral application of HF for orthodontic treatment.
Material and methods
Leucite (LEU) and lithium disilicate (LiSi) specimens were pretreated with (i) 4% hydrofluoric acid + silane (HF), (ii) Monobond Etch&Prime (MEP), (iii) silicatization + silane (CoJet), and (iv) SiC grinder + silane (SiC). Molars etched (phosphoric acid) and conditioned acted as comparison group. SBS was measured after 24 h (distilled water, 37 °C), 500 × thermocycling (5/55 °C), and 90 days (distilled water, 37 °C). Data was analyzed using Shapiro-Wilk, Kruskal-Wallis with Dunn's post hoc test and Bonferroni correction, Mann-Whitney U, and Chi2 test (p < 0.05). The adhesive remnant index (ARI) was determined.
Methods
Leucite (LEU) and lithium disilicate (LiSi) specimens were pretreated with (i) 4% hydrofluoric acid + silane (HF), (ii) Monobond Etch&Prime (MEP), (iii) silicatization + silane (CoJet), and (iv) SiC grinder + silane (SiC). Molars etched (phosphoric acid) and conditioned acted as comparison group. SBS was measured after 24 h (distilled water, 37 °C), 500 × thermocycling (5/55 °C), and 90 days (distilled water, 37 °C). Data was analyzed using Shapiro-Wilk, Kruskal-Wallis with Dunn's post hoc test and Bonferroni correction, Mann-Whitney U, and Chi2 test (p < 0.05). The adhesive remnant index (ARI) was determined.
Objective
The study aims to investigate the shear bond strength (SBS) between silicate ceramic restorations and ceramic brackets after different pretreatments and aging
Results
LEU pretreated with MEP showed lower SBS than pretreated with HF, CoJet, or SiC. LiSi pretreated with MEP resulted in lower initial SBS than pretreated with HF or SiC. After thermocycling, pretreatment using MEP led to lower SBS than with CoJet. Within LiSi group, after 90 days, the pretreatment using SiC resulted in lowest SBS values. After HF and MEP pretreatment, LEU showed lower initial SBS than LiSi. After 90 days of water storage, within specimens pretreated using CoJet or SiC showed LEU higher SBS than LiSi. Enamel presented higher or comparable SBS values to LEU and LiSi. With exception of MEP pretreatment, ARI 3 was predominantly observed, regardless the substrate, pretreatment, and aging level. Conclusions: MEP pretreatment presented the lowest SBS values, regardless the silicate ceramic and aging level. Further research is necessary. Clinical relevance: There is no need for intraoral application of HF for orthodontic treatment.