Abstract
Free-standing and flexible field-effect transistors based on 6,13-bis(triisopropylsilylethynyl)-pentacene (TIPS-pentacene)/polystyrene bilayers are obtained by well-controlled phase separation of both components. The phase separation is induced by solvent vapor annealing of initially amorphous blend films, leading to crystallization of TIPS-pentacene as the top layer. The crystallinity and blend morphology strongly depend on the molecular weight of polystyrene, and under optimized conditions, distinct phase separation with a well-defined and trap-free interface between both fractions is achieved. Due to the distinct bilayer morphology, the resulting flexible field-effect transistors reveal similar charge carrier mobilities as rigid devices and additionally pronounced environmental and bias stress stabilities. The performance of the flexible transistors remains stable up to a strain of 1.8%, while above this deformation, a close relation between current and strain is observed that is required for applications in strain sensors.