Conclusion
Co-electrospun PCL-nHA with gelatin as a sacrificial agent in combination with ultrasonication may be an effective, economic and controllable method to increase the pore size in electrospun scaffolds for bone tissue engineering applications.
Methods
After electrospinnig, gelatin was washed with water, and the prepared scaffold was ultrasonicated. Morphological and structural properties of the prepared scaffolds were studied by SEM. Fourier transform infrared (FTIR) spectroscopy and water contact angle analysis were used to evaluate the removal of gelatin.
Results
According to the SEM results, the pore size of the modified scaffolds was increased 3-folds compared to the control sample. For PCL-nHA gelatin: (80:20) after the treatment, the average cell infiltration was 42.7 μm, while there was no infiltration for the control group. The modified electrospun scaffold significantly enhanced the osteogenic differentiation of hBMSCs as verified by increased ALP activity and upregulation of runt-related transcription factor 2 (RUNX2), collagen type 1 (COL1) and osteocalcin (OCN) genes.