Abstract
OBJECTIVE: Polymethyl methacrylate (PMMA) is one of the most widely used denture base material because of favorable esthetics and desirable characteristics such as easy handling. Acrylic resins, although, have some inherent disadvantages such as relatively poor physical and mechanical properties. The objective of the present study was to evaluate and compare the impact strength of unmodified and modified heat cure PMMA-based denture base material with addition of different concentrations of silver nanoparticles (AgNPs) (0.5, 1, 2 wt%). METHODS: The present in-vitro study comprised of a total of 60 samples allocated to four groups with Group A samples consisting of heat cure acrylic resin without any modification (used as control); Group B samples consisting of heat cure acrylic resin modified with 0.5 wt% of AgNPs; and subsequently, Group C and Group D samples consisting of heat cure acrylic resin modified with 1 wt% and 2 wt% of AgNPs, respectively. The impact strength of the prepared acrylic samples was evaluated using Izod/Charpy Impact Tester, while the values obtained were tabulated and subjected to statistical analysis. Statistical analysis was done using Statistical Package for Social Sciences (SPSS) version 17.0 (SPSS Inc., Chicago, IL, USA), while one-way analysis of variance and Tukey's multiple post-hoc procedures were used for statistical analysis. P < .05 was considered statistically significant. RESULTS: The highest impact strength was found in Group C samples consisting of heat cure acrylic resin modified with 1 wt% of AgNPs to be closely followed by Group B samples consisting of heat cure acrylic resin modified with 0.5 wt% of AgNPs. Group D samples consisting of heat cure acrylic resin modified with 2 wt% of AgNPs, although, revealed relatively lower impact strength compared to Group B and Group C samples. CONCLUSIONS: Within the limitations of the present study, it was concluded that the impact strength of mechanically modified heat polymerized PMMA resin was significantly enhanced with addition of varying concentrations of AgNPs, although, it was observed that with an increase in the concentration of AgNPs, a subsequent decrease in the tensile strength of the final polymer material was observed.