Abstract
OBJECTIVE: To investigate the effect of different intracoronal bleaching methods on the shear bond strength and site of failure of ceramic brackets. MATERIALS AND METHODS: Sixty freshly extracted human maxillary incisors were randomly divided into four groups (n = 15). Endodontic access cavity was prepared and root canals were filled, root fillings were removed 2mm apical to the cementoenamel junction, and a 2-mmthick layer of glass ionomer cement base was applied. Group 1 served as the control. Intracoronal bleaching was performed with 35% carbamide peroxide in group 2, sodium perborate in group 3, and 37.5% hydrogen peroxide in group 4. The teeth were immersed in artificial saliva for 4 weeks before bracket bonding. Ceramic brackets were bonded with composite resin and cured with LED light. After bonding, the shear bond strength of the brackets was tested with a universal testing machine. The site of bond failure was determined by modified ARI (Adhesive Remnant Index). RESULTS: The highest value of shear bond strength was measured in control group (18.67 ± 1.59 MPa), which was statistically significant from groups 2,3, and 4. There was no significant difference between groups 2 and 4. The lowest shear bond strength was measured in group 3. ARI scores were not significant from each other. CONCLUSIONS: Intracoronal bleaching significantly affected the shear bond strength of ceramic brackets even after 4 weeks of bleaching. Bleaching with sodium perborate affects shear bond strength more adversely than does bleaching with other agents like hydrogen peroxide and carbamide peroxide.