Abstract
This study aims to explore the static mechanical characteristics of coral aggregate seawater shotcrete (CASS) using an appropriate mix proportion. The orthogonal experiments consisting of four-factor and three-level were conducted to explore an optimal mix proportion of CASS. On a macro-scale, quasi-static compression and splitting tests of CASS with optimal mix proportion at various curing ages employed a combination of acoustic emission (AE) and digital image correlation (DIC) techniques were carried out using an electro-hydraulic servo-controlled test machine. A comparative analysis of static mechanical properties at different curing ages was conducted between the CASS and ordinary aggregate seawater shotcrete (OASS). On a micro-scale, the numerical specimens based on particle flow code (PFC) were subjected to multi-level microcracks division for quantitive analysis of the failure mechanism of specimens. The results show that the optimal mix proportion of CASS consists of 700 kg/m(3) of cementitious materials content, a water-binder ratio of 0.45, a sand ratio of 60%, and a dosage of 8% for the accelerator amount. The tensile failure is the primary failure mechanism under uniaxial compression and Brazilian splitting, and the specimens will be closer to the brittle material with increased curing age. The Brazilian splitting failure caused by the arc-shaped main crack initiates from the loading points and propagates along the loading line to the center. Compared with OASS, the CASS has an approximately equal early and low later strength mainly because of the minerals' filling or unfilling effect on coral pores. The rate of increase in CASS is swifter during the initial strength phase and decelerates during the subsequent stages of strength development. The failure in CASS is experienced primarily within the cement mortar and bonding surface between the cement mortar and aggregate.