Abstract
Hygrothermal treatment is an environmentally friendly and efficient modification method. In this study, Moso bamboo was modified with hygrothermal treatments, and the results of nitrogen adsorption, X-ray diffraction (XRD), scanning electron microscopy (SEM) and nano indentation (NI) were then examined. Interestingly, the samples that underwent hygrothermal treatment at 180 °C and 117% RH (relative humidity) had the highest crystallinity (36.92%), which was 11.07% statistically larger than that of the control samples. Simultaneously, the total pore volume and average pore diameter (2.72 nm) dramatically decreased by 38.2% and 43.7%, respectively. The NI elasticity and hardness of the samples also reached the highest values under this condition; both increased by nearly 21% as compared with the control samples. Therefore, 180 °C is a favorable hygrothermal treatment temperature for Moso bamboo modification due to the porosity changes and the improvement of the nanomechanics of the cell walls.