Abstract
OBJECTIVE: Extracorporeal circulation devices are coated with a biocompatible polymer coating agent (BPCA) that has a hydrophilic blood-contacting layer, but hemofilters are not. We aimed to investigate the antithrombotic properties of a BPCA-coated hemofilter. METHODS: Four experiments using BPCA-coated circuits and non-coated hemofilters and four experiments using BPCA-coated circuits and BPCA-coated hemofilters were performed with whole human blood and compared by measuring the circuit pressure every 5 min, antithrombin activity every 40 min, and thrombin-antithrombin complex every 40 min, for a total of 240 min of recirculation. RESULTS: The mean time required for the pressure at the inlet of the hemofilter to increase sharply was longer in BPCA-coated than in non-coated hemofilters (66 ± 11 min vs 25 ± 9 min, p < 0.01). The mean antithrombin activity value at 200 and 240 min of recirculation was significantly higher in the experiments with BPCA-coated versus non-coated hemofilters (43.3 ± 2.87 vs 33.3 ± 5.74, p = 0.04; 42.8 ± 3.59 vs 31.0 ± 5.35, p = 0.01, respectively); the antithrombin activity values at the other time points were not significantly different. Furthermore, all thrombin-antithrombin complex values in experiments with the BPCA-coated hemofilters achieved overrange at 80 min of recirculation, whereas those with the non-coated hemofilter achieved overrange at 40 min. CONCLUSION: This study suggests that BPCA-coated hemofilters can inhibit antithrombin consumption, contributing to antithrombotic effects in extracorporeal circulation circuits.