Abstract
Highly-aligned flake graphite (FG) reinforced Cu matrix composites with high thermal conductivity and adaptive coefficient of thermal expansion were successfully prepared via the collaborative process of tape-casting and hot-pressing sintering. To overcome the problem of fragile interface, Zr-Cu alloy powder was introduced instead of pure Zr powder to enhance the interfacial strength, ascribed to the physical-chemical bonding at the Cu-FG interface. The results indicate that the synthetic ZrC as interfacial phase affects the properties of FG/Cu composites. The thermal conductivity reaches the maximum value of 608.7 W/m∙K (52% higher than pure Cu) with 0.5 wt % Zr. Surprisingly, the negative coefficient of thermal expansion (CTE) in the Z direction is acquired from -7.61 × 10-6 to -1.1 × 10-6/K with 0 to 2 wt % Zr due to the physical mechanism of strain-engineering of the thermal expansion. Moreover, the CTE in X-Y plane with Zr addition is 8~10 × 10-6/K, meeting the requirements of semiconductor materials. Furthermore, the bending strength of the FG/Cu-2 wt % Zr composite is 42% higher than the FG/Cu composite. Combining excellent thermal conductivity with ultralow thermal expansion make the FG/Cu-Zr composites be a highly promising candidate in the electronic packaging field.