Abstract
The object was to enhance the bioactivity of pure polyether-ether-ketone (PEEK) by incorporating nano-TiO2 (n-TiO2) and investigate its potential mechanism. PEEK/n-TiO2 composite was manufactured using a 3D PEEK printer and characterized by scanning electron microscopy (SEM), 3D profiler, energy-dispersive spectroscopy, and Fourier-transform infrared (FT-IR) analyses. Cytocompatibility was tested using SEM, fluorescence, and cell counting kit-8 assays. Osteogenic differentiation was evaluated by osteogenic gene and mineralized nodule levels. The expression of the candidate miRNAs were detected in composite group, and its role in osteogenic differentiation was studied. As a results the 3D-printed PEEK/n-TiO2 composite (Φ = 25 mm, H = 2 mm) was successfully fabricated, and the TiO2 nanoparticles were well distributed and retained the nanoscale size of the powder. The Ra value of the composite surface was 2.69 ± 0.29, and Ti accounted for 22.29 ± 12.09% (in weight), and FT-IR analysis confirmed the characteristic peaks of TiO2. The cells in the composite group possessed better proliferation and osteogenic differentiation abilities than those in the PEEK group. miR-154-5p expression was decreased in the composite group, and the inhibition of miR-154-5p significantly enhanced the proliferation and osteogenic differentiation abilities. In conclusion, 3D-printed PEEK/n-TiO2 composite enhanced cytocompatibility and osteogenic induction ability by downregulating miR-154-5p, which provides a promising solution for improving the osteointegration of PEEK.