Abstract
ConspectusGalvanic replacement synthesis involves oxidation and dissolution of atoms from a substrate while the salt precursor to another material with a higher reduction potential is reduced and deposited on the substrate. The driving force or spontaneity of such a synthesis comes from the difference in reduction potential between the redox pairs involved. Both bulk and micro/nanostructured materials have been explored as substrates for galvanic replacement synthesis. The use of micro/nanostructured materials can significantly increase the surface area, offering immediate advantages over the conventional electrosynthesis. The micro/nanostructured materials can also be intimately mixed with the salt precursor in a solution phase, resembling the setting of a typical chemical synthesis. The reduced material tends to be directly deposited on the surface of the substrate, just like the situation in an electrosynthesis. Different from an electrosynthesis where the two electrodes are spatially separated by an electrolyte solution, the cathodes and anodes are situated on the same surface, albeit at different sites, even for a micro/nanostructured substrate. Since the oxidation and dissolution reactions occur at sites different from those for reduction and deposition reactions, one can control the growth pattern of the newly deposited atoms on the same surface of a substrate to access nanostructured materials with diverse and controllable compositions, shapes, and morphologies in a single step. Galvanic replacement synthesis has been successfully applied to different types of substrates, including those made of crystalline and amorphous materials, as well as metallic and nonmetallic materials. Depending on the substrate involved, the deposited material can take different nucleation and growth patterns, resulting in diverse but well-controlled nanomaterials sought for a variety of studies and applications.In this Account, we recapitulate our efforts over the past two decades in fabricating metal nanostructures for a broad range of applications by leveraging the unique capability of galvanic replacement synthesis. We begin with a brief introduction to the fundamentals of galvanic replacement between metal nanocrystals and salt precursors, followed by a discussion of the roles played by surface capping agents in achieving site-selected carving and deposition for the fabrication of various bimetallic nanostructures. Two examples based on the Ag-Au and Pd-Pt systems are selected to illustrate the concept and mechanism. We then highlight our recent work on the galvanic replacement synthesis involving nonmetallic substrates, with a focus on the protocol, mechanistic understanding, and experimental control for the fabrication of Au- and Pt-based nanostructures with tunable morphologies. Finally, we showcase the unique properties and applications of nanostructured materials derived from galvanic replacement reactions for biomedicine and catalysis. We also offer some perspectives on the challenges and opportunities in this emerging field of research.