Abstract
The lateral size of graphene nanosheets plays a critical role in the properties and microstructure of 3D graphene as well as their application as supports of electrocatalysts for CO(2) reduction reactions (CRRs). Here, graphene oxide (GO) nanosheets with different lateral sizes (1.5, 5, and 14 µm) were utilized as building blocks for 3D graphene aerogel (GA) to research the size effects of GO on the CRR performances of 3D Au/GA catalysts. It was found that GO-L (14 µm) led to the formation of GA with large pores and a low surface area and that GO-S (1.5 µm) induced the formation of GA with a thicker wall and isolated pores, which were not conducive to the mass transfer of CO(2) or its interaction with catalysts. Au/GA constructed with a suitable-sized GO (5 µm) exhibited a hierarchical porous network and the highest surface area and conductivity. As a result, Au/GA-M exhibited the highest Faradaic efficiency (FE) of CO (FE(CO) = 81%) and CO/H(2) ratio at -0.82 V (vs. a Reversible Hydrogen Electrode (RHE)). This study indicates that for 3D GA-supported catalysts, there is a balance between the improvement of conductivity, the adsorption capacity of CO(2), and the inhibition of the hydrogen evolution reaction (HER) during the CRR, which is related to the lateral size of GO.