Abstract
In recent years, nanoporous Si films have been widely studied for thermoelectric applications due to the low cost and earth abundance of Si. Despite many encouraging results, inconsistency still exists among experimental and theoretical studies of reduced lattice thermal conductivity for varied nanoporous patterns. In addition, divergence can also be found among reported data, due to the difference in sample preparation and measurement setups. In this work, systematic measurements are carried out on nanoporous Si thin films with pore pitches on the order of 100 nm, where pores are drilled either by dry etching or a focused ion beam. In addition to thermal conductivity measurements, the specific heat of the nanoporous films is simultaneously measured and agrees with the estimation using bulk values, indicating a negligible change in the phonon dispersion. Without considering coherent phonon transport, the measured thermal conductivity values agree with predictions by frequency-dependent phonon Monte Carlo simulations assuming diffusive pore-edge phonon scattering. In Monte Carlo simulations, an expanded effective pore diameter is used to account for the amorphization and oxidation on real pore edges.