Abstract
Polyelectrolyte complex (PEC) films such as polyelectrolyte multilayers have demonstrated excellent oxygen barrier properties, but unfortunately, the established layer-by-layer approaches are laborious and difficult to scale up. Here, we demonstrate a novel single-step approach to produce a PEC film, based on the use of a volatile base. Ammonia was used to adjust the pH of poly(acrylic acid) (PAA) so that direct complexation was avoided when it was mixed with polyethylenimine (PEI). Different charge ratios of homogeneous PEI/PAA solutions were successfully prepared and phase diagrams varying the concentration of ammonia or polyelectrolyte were made to study the phase behavior of PEI, PAA, and ammonia in water. Transparent ∼1 μm thick films were successfully deposited on biaxially orientated polypropylene (BOPP) sheets using a Meyer rod. After casting the films, the decrease in pH, caused by the evaporation of ammonia, triggered the complexation during drying. The oxygen permeation properties of films with different ratios and single polyelectrolytes were tested. All films displayed excellent oxygen barrier properties, with an oxygen permeation below 4 cm(3)·m(-2)·day(-1)·atm(-1) (<0.002 barrer) at the optimum ratio of 2:1 PEI/PAA. This ammonia evaporation-induced complexation approach creates a new pathway to prepare PEC films in one simple step while allowing the possibility of recycling.