Significance
Fretting wear and corrosion within the implant's modular taper junction are prominent causes of implant failure, as they promote the release of corrosion products and subsequent development of adverse local tissue reactions. Being a multifactorial process, several in vitro models have been developed to recreate the in vivo corrosion process, often summarized as mechanically-assisted crevice corrosion. Considering the excellent corrosion properties of CoCrMo alloy, the severity of chemically-generated damage observed at the modular interface has been surprising and poorly understood. The aim of the current study is to provide a better understanding of macrophages and their plasticity at the THR taper interface when they encounter wear debris from CoCrMo alloy. This is a preliminary study along the path towards determining the mechanism(s) of CAC.
Statement of significance
Fretting wear and corrosion within the implant's modular taper junction are prominent causes of implant failure, as they promote the release of corrosion products and subsequent development of adverse local tissue reactions. Being a multifactorial process, several in vitro models have been developed to recreate the in vivo corrosion process, often summarized as mechanically-assisted crevice corrosion. Considering the excellent corrosion properties of CoCrMo alloy, the severity of chemically-generated damage observed at the modular interface has been surprising and poorly understood. The aim of the current study is to provide a better understanding of macrophages and their plasticity at the THR taper interface when they encounter wear debris from CoCrMo alloy. This is a preliminary study along the path towards determining the mechanism(s) of CAC.