Abstract
All polymers exhibit gas permeability through the free volume of entangled polymer chains(1-3). By contrast, two-dimensional (2D) materials including graphene stack densely and can exhibit molecular impermeability(4-6). Solution-synthesized 2D polymers that exhibit the latter by poly-condensation have been a longstanding goal. Herein, we demonstrate self-supporting, spin-coated 2D polyaramid nanofilms that exhibit nitrogen permeability below 3.1 × 10(-)(9) Barrer, nearly four orders of magnitude lower than every class of existing polymer, and similar for other gases tested (helium, argon, oxygen, methane and sulfur hexafluoride). Optical interference during the pressurization of nanofilm-coated microwells allows measurement of mechanosensitive rim opening and sealing, creating gas-filled bulges that are stable exceeding three years. This discovery enables 2D polymer resonators with high resonance frequencies (about 8 MHz) and quality factors up to 537, similar to graphene. A 60-nm coating of air-sensitive perovskites reduces the lattice degradation rate 14-fold with an oxygen permeability of 3.3 × 10(-8) Barrer. Molecularly impermeable polymers promise the next generation of barriers that are synthetically processable, chemically amenable and maximize molecular rejection with minimal material, ultimately advancing sustainability goals.