Abstract
In the present study, post-heat treatment was applied to improve the mechanical and tribological performance of 3D-printed polymer components. Two polymers, i.e., polylactic acid (PLA) and polyether ether ketone (PEEK), were used as base materials. Re-entrant structures were incorporated into printed specimens to mitigate friction-induced vibrations (FIV). The results showed that the heat-treatment process effectively enhanced the mechanical properties of both materials by increasing their elastic modulus and yield strength. Specifically, the tensile and compressive strengths of heat-treated PLA increased from 44.14 MPa to 47.66 MPa and from 68 MPa to 82 MPa, respectively. A similar trend was observed for heat-treated PEEK, with tensile strength increasing from 75.53 MPa to 84.91 MPa and compressive strength from 106 MPa to 123 MPa. Furthermore, the increased stiffness enabled the re-entrant structures to more effectively reduce FIV during the sliding process of specimens. However, heat treatment produced contrasting effects on the wear performance of the two polymers. The specific wear rate of the heat-treated PLA sample with the re-entrant structure increased from 2.36 × 10(-5) mm(3)/(N · m) to 4.5 × 10(-4) mm(3)/(N · m), while it decreased for the PEEK sample from 3.18 × 10(-6) mm(3)/(N · m) to 6.2 × 10(-7) mm(3)/(N · m). Microscopic observations revealed that this difference was due to the variations in the brittleness of the treated materials, which influenced wear-debris formation and the development of the transfer film on the steel counterface. These findings demonstrate that post-heat treatment is an effective method for tailoring and optimizing the mechanical behavior of printed polymers while also emphasizing the necessity of systematically evaluating its influence on the tribological performance of printed engineering parts subjected to different sliding conditions.